530G
LDPE
Thermoplastic-Polyethylene-Ldpe
한화토탈에너지스
| Machanical | Value | Unit | Condition | Method |
|---|---|---|---|---|
| Elongation At Break | 700 | % | 50mm/min | ASTM D638 |
| Tensile Strength At Yield | 12.74884 | MPa | 50mm/min | ASTM D638 |
| Tensile Strength At Break | 12.74884 | MPa | 50mm/min | ASTM D638 |
| Physical | Value | Unit | Condition | Method |
|---|---|---|---|---|
| Melt Index | 2.8 | g/10min | 190℃, 2.16kg | ASTM D1238 |
| Coefficient Of Friction | 0.05 | ASTM D1894 | ||
| Density | 0.925 | g/㎤ | ASTM D1505 |
| Thermal | Value | Unit | Condition | Method |
|---|---|---|---|---|
| Softening Temperature | 95 | ˚C | 1kg | ASTM D1525 |
| Melting Temp | 112.5 | ˚C | SGC method | |
| Brittleness Temp. | ˚C | ASTM D746 |
| Optical | Value | Unit | Condition | Method |
|---|---|---|---|---|
| Haze | 7 | % | ASTM D1003 |
| Other | Value | Unit | Condition | Method |
|---|---|---|---|---|
| Blocking | 240 | g | SGC Method |