PC-1280R
PC
Thermoplastic-Polycarbonate-Pc
롯데케미칼
| Machanical | Value | Unit | Condition | Method |
|---|---|---|---|---|
| Tensile Strength At Yield | 61.78284 | MPa | ASTM D638 | |
| Elongation At Break | 60 | % | ASTM D638 | |
| Flexural Strength | 90.22256 | MPa | ASTM D790 | |
| Izod Impact Strength(Astm) | 686.42798 | J/m | ASTM D256 | |
| Rockwell Hardness | 70 | M scale | ASTM D785 | |
| Flexural Modulus | 2353.632 | MPa | ASTM D790 |
| Physical | Value | Unit | Condition | Method |
|---|---|---|---|---|
| Specific Gravity | 1.2 | ASTM D792 | ||
| Melt Index | 28 | g/10min | ASTM D1238 | |
| Water Absorption | 0.2 | % | ASTM D955 |
| Thermal | Value | Unit | Condition | Method |
|---|---|---|---|---|
| Softening Temperature | 150 | ˚C | ASTM D1525 | |
| Heat Deflection Temperature @0.46mpa | 139 | ˚C | ASTM D648 | |
| Heat Deflection Temperature @1.82mpa | 128 | ˚C | ASTM D648 | |
| Coefficient Of Thermal Expansion(Cte) | 0.00006 | 1/˚C | ASTM D696 |
| Electrical | Value | Unit | Condition | Method |
|---|---|---|---|---|
| Dielectric Constant | 2.95 | ASTM D150 | ||
| Volume Resistivity | 100000000000000 | Ωcm | ASTM D257 |
| Optical | Value | Unit | Condition | Method |
|---|---|---|---|---|
| Refractive Index | 1.585 | ASTM D542 | ||
| Transmittance | 89 | % | ASTM D1003 | |
| Haze | % | ASTM D1003 |
| Other | Value | Unit | Condition | Method |
|---|---|---|---|---|
| Mold Shrinkage | 0.5 | % | ASTM D955 |