HDPE JK910
HDPE
Thermoplastic-Polyethylene-Hdpe
SK지오센트릭
| Machanical | Value | Unit | Condition | Method |
|---|---|---|---|---|
| Flexural Modulus | 902.21 | MPa | ASTM D790 | |
| Izod Impact Strength(Astm), Notched | 40 | J/m | 23°C | ASTM D256 |
| Elongation At Break | 220 | % | ASTM D638 | |
| Tensile Strength At Break | 4.9 | MPa | ASTM D638 | |
| Tensile Strength At Yield | 25.5 | MPa | ASTM D638 |
| Physical | Value | Unit | Condition | Method |
|---|---|---|---|---|
| Density | 0.961 | g/㎤ | ASTM D1505 | |
| Melt Index | 20 | g/10min | ASTM D1238 |
| Thermal | Value | Unit | Condition | Method |
|---|---|---|---|---|
| Brittleness Temp. | ˚C | ASTM D746 | ||
| Softening Temperature | 123 | ˚C | ASTM D1525 |