Iupiace® AH40

Iupiace
MPPO
Thermoplastic-Polyphenylenes-Mppo

Mitsubishi Engineering-Plastics

Machanical Value Unit Condition Method
Tensile Strength At Yield 43 MPa ISO 527-1/2
Charpy Impact Strength(Iso) 153 kJ/㎡ 23℃ ISO 179-1/2
Nominal Strain At Break 34 % ISO 527-1/2
Flexural Strength 76 MPa ISO 178
Elongation At Yield 3.2 % ISO 527-1/2
Charpy Impact Strength(Iso), Notched 17 kJ/㎡ 23℃ ISO 179-1/2
Flexural Modulus 2500 MPa ISO 178
Tensile Modulus 2500 MPa ISO 527-1/2
Physical Value Unit Condition Method
Water Absorption 0.07 % 23℃, Underwater
Density 1.06 g/㎤ ISO 1183
Melt Volume-Flow Rate 17 ㎤/10min 300℃, 2.16kgf ISO 1133
Thermal Value Unit Condition Method
Heat Deflection Temperature @0.46mpa 110 ˚C ISO 75-1/2
Coefficient Of Thermal Expansion(Cte) 0.000067 1/˚C MD ISO 11359-2
Coefficient Of Thermal Expansion(Cte) 0.000071 1/˚C TD ISO 11359-2
Heat Deflection Temperature @1.82mpa 95 ˚C ISO 75-1/2
Flammability Value Unit Condition Method
Flammability -9 class 0.75mm UL94
Electrical Value Unit Condition Method
Surface Resistivity 2000000000000000 Ω/sq. IEC 60093
Dielectric Strength 20 kV/mm 3mmt IEC 60243­1
Volume Resistivity 30000000000000000 Ωcm IEC 60093
Dielectric Strength 38 kV/mm 1mmt IEC 60243­1
Other Value Unit Condition Method
Mold Shrinkage 0.5 % TD, 3mmt
Mold Shrinkage 0.5 % MD, 3mmt