HI 425TVL
HIPS
Thermoplastic-Styrenics_Polymers-Hips
금호석유화학
| Machanical | Value | Unit | Condition | Method |
|---|---|---|---|---|
| Izod Impact Strength(Astm), Notched | 93.16 | J/m | 23˚C | ASTM D256 |
| Flexural Strength | 29.42 | MPa | 23℃ | ASTM D790 |
| Elongation At Break | 40 | % | 50mm/min | ASTM D638 |
| Rockwell Hardness | 60 | L-scale | ASTM D785 | |
| Tensile Strength At Break | 23.54 | MPa | 50mm/min | ASTM D638 |
| Flexural Modulus | 1618.12 | MPa | 23℃ | ASTM D790 |
| Physical | Value | Unit | Condition | Method |
|---|---|---|---|---|
| Water Absorption | 0.05 | % | 24hr in the water | ASTM D570 |
| Melt Index | 13 | g/10min | 200℃, 5.0kg | ASTM D1238 |
| Specific Gravity | 1.04 | 23℃ | ASTM D792 |
| Thermal | Value | Unit | Condition | Method |
|---|---|---|---|---|
| Softening Temperature | 95 | ˚C | ASTM D1525 | |
| Heat Deflection Temperature @1.82mpa | 76 | ˚C | ASTM D648 |
| Flammability | Value | Unit | Condition | Method |
|---|---|---|---|---|
| Flammability | -9 | class | 1.6mm | UL No. E65424 |
| Other | Value | Unit | Condition | Method |
|---|---|---|---|---|
| Mold Shrinkage | 0.3 | % | ASTM D955 |