Terluran® GP-35
Terluran®
ABS
Thermoplastic-Styrenics_Polymers-Abs
BASF
| Machanical | Value | Unit | Condition | Method |
|---|---|---|---|---|
| Elongation At Yield | 2.4 | % | ISO 527 | |
| Tensile Modulus | 2400 | MPa | 100% | ISO 527 |
| Flexural Strength | 65 | MPa | ISO 178 | |
| Hardness Of Ball Indetation | 99 | MPa | ISO 2039-1 | |
| Izod Impact Strength(Astm), Notched | 215.745508 | J/m | 23℃ | ASTM D256A |
| Izod Impact Strength(Astm), Notched | 240 | J/m | 23℃ | ASTM D256 |
| Tensile Strength At Yield | 44 | MPa | ISO 527 | |
| Charpy Impact Strength(Iso), Notched | 7 | kJ/㎡ | -30℃ | ISO 179/1eA |
| Charpy Impact Strength(Iso), Unnotched | 150 | kJ/㎡ | 23℃ | ISO 179/1eU |
| Charpy Impact Strength(Iso), Unnotched | 155 | kJ/㎡ | -30℃ | ISO 179/1eU |
| Charpy Impact Strength(Iso), Notched | 22 | kJ/㎡ | 23℃ | ISO 179/1eA |
| Izod Impact Strength(Astm), Notched | 80 | J/m | -30℃ | ASTM D256 |
| Physical | Value | Unit | Condition | Method |
|---|---|---|---|---|
| Melt Volume-Flow Rate | 35 | ㎤/10min | 220℃, 10kg | ISO 1133 |
| Water Absorption | 0.24 | % | 23℃, 50% RH | |
| Water Absorption | 0.95 | % | ISO 62 | |
| Density | 1.04 | g/㎤ | ISO 1183 |
| Thermal | Value | Unit | Condition | Method |
|---|---|---|---|---|
| Heat Deflection Temperature @1.82mpa | 94 | ˚C | ISO 75-2 | |
| Softening Temperature | 95 | ˚C | VST/B/50 | ISO 306 |
| Thermal Conductivity | 0.17 | W/mK | DIN 52 612 | |
| Coefficient Of Thermal Expansion(Cte) | 0.00008 | 1/˚C | DIN 53 752 | |
| Softening Temperature | 102 | ˚C | VST/A/50 | ISO 306 |
| Heat Deflection Temperature @0.46mpa | 99 | ˚C | ISO 75-2 |
| Flammability | Value | Unit | Condition | Method |
|---|---|---|---|---|
| Flammability | -9 | class | 3.2mm | UL94 |
| Flammability | -9 | class | 1.6mm | UL94 |
| Electrical | Value | Unit | Condition | Method |
|---|---|---|---|---|
| Volume Resistivity | 10000000000000 | Ωcm | ISO IEC 93 |
| Other | Value | Unit | Condition | Method |
|---|---|---|---|---|
| Processing Temperature | 220 | ˚C |