LUPOY PC 1300-10

PC
Thermoplastic-Polycarbonate-Pc

LG화학

Machanical Value Unit Condition Method
Flexural Modulus 2410 MPa ASTM D790
Izod Impact Strength(Astm), Notched 900 J/m 23℃ ASTM D256
Rockwell Hardness 73 M scale ASTM D785
Instrumented Dart Impact Strength 87 J Total Energy, 23℃ ASTM D3763
Izod Impact Strength(Astm), Unnotched 10000000000 J/m 23℃ ASTM D256
Flexural Strength 96 MPa ASTM D790
Tensile Modulus 2410 MPa ASTM D638
Elongation At Yield 6 % ASTM D638
Taber Abrasion 45 % ASTM D1044
Elongation At Break 150 % ASTM D638
Tensile Strength At Yield 60 MPa ASTM D638
Tensile Strength At Break MPa ASTM D638
Physical Value Unit Condition Method
Water Absorption 0.32 % equilibrium, 50%RH, 23℃ ASTM D570
Density 1.2 g/㎤ ASTM D792
Melt Index 10 g/10min 300℃, 1.2kg ASTM D1238
Water Absorption 0.15 % 24hr, 23℃ ASTM D570
Thermal Value Unit Condition Method
Coefficient Of Thermal Expansion(Cte) 0.000068 1/˚C -40 to 82℃ ASTM D696
Heat Deflection Temperature @1.82mpa 141 ˚C ASTM D648
Heat Deflection Temperature @0.46mpa 144 ˚C ASTM D648
Heat Deflection Temperature @1.82mpa 128 ˚C ASTM D648
Softening Temperature 149 ˚C 50℃/hr, 50N Load ASTM D1525
Temp-Ball Indentation 125 ˚C IEC 598-1
Flammability Value Unit Condition Method
Flammability -6 class 2.5-2.7mm ASTM D635
Flammability -6 class 1.6mm ASTM D635
Flammability -9 class 3.0mm ASTM D635
Flammability -6 class 0.5mm ASTM D635
Limiting Oxygen Index 26 % ASTM D2863
Electrical Value Unit Condition Method
Volume Resistivity 200000000000000000 Ωcm 23℃, dry ASTM D257
Dissipation Factor 0.001 60Hz ASTM D150
Dielectric Constant 3 60Hz ASTM D150
Dielectric Breakdown Strength 17 kV/mm ASTM D149
Glow Wire Test 850 ˚C 2.0mm, 5sec IEC 695-2-1
Comparative Tracking Index(Cti) 250 V 2.0mm IEC 112
Optical Value Unit Condition Method
Transmittance 89 % Light ASTM D1003
Refractive Index 1.586 ASTM D542
Haze 0.7 % ASTM D1003
Other Value Unit Condition Method
Mold Shrinkage 0.5 % ASTM D955
Acidity Of Combustion Gas 25 mm ASTM D635